by N. G. Chechenin, E. H. du Marchie van Voorthuysen, J. Th. M. De Hosson and D. O. Boerma
Abstract:
Variations of phase composition and magnetic properties of electrodeposited nanocrystalline Co–Fe–Ni films with film thickness in the range of 50–500nm were analyzed. The samples were magnetically soft with coercivity in the range Hc=2–20Oe and uniaxial magnetic anisotropy up to Hk=20Oe. It was found that Hc decreases and Hk increases with increasing film thickness. The BCC phase dominates at small film thickness up to about 80nm and the FCC phase increases when the film growths to a larger thickness. The increase of FCC phase correlates with the improvement of the ultrasoft magnetic properties.
Reference:
N. G. Chechenin, E. H. du Marchie van Voorthuysen, J. Th. M. De Hosson and D. O. Boerma, “Variation of structure and magnetic properties with thickness of thin Co59Fe26Ni15 films”, Journal of Magnetism and Magnetic Materials, vol. 290-291, pp. 1539–1542.
Bibtex Entry:
@article{chechenin_variation_2005,
series = {Proceedings of the {Joint} {European} {Magnetic} {Symposia} ({JEMS}' 04)},
title = {Variation of structure and magnetic properties with thickness of thin {Co59Fe26Ni15} films},
volume = {290-291},
issn = {0304-8853},
url = {https://www.sciencedirect.com/science/article/pii/S0304885304014830},
doi = {10.1016/j.jmmm.2004.11.247},
abstract = {Variations of phase composition and magnetic properties of electrodeposited nanocrystalline Co–Fe–Ni films with film thickness in the range of 50–500nm were analyzed. The samples were magnetically soft with coercivity in the range Hc=2–20Oe and uniaxial magnetic anisotropy up to Hk=20Oe. It was found that Hc decreases and Hk increases with increasing film thickness. The BCC phase dominates at small film thickness up to about 80nm and the FCC phase increases when the film growths to a larger thickness. The increase of FCC phase correlates with the improvement of the ultrasoft magnetic properties.},
language = {en},
urldate = {2021-07-13},
journal = {Journal of Magnetism and Magnetic Materials},
author = {Chechenin, N. G. and du Marchie van Voorthuysen, E. H. and De Hosson, J. Th. M. and Boerma, D. O.},
month = apr,
year = {2005},
keywords = {Anisotropy, Co–Fe–Ni, Coercivity, Microstructure, Nanocrystalline thin films, Phase composition, Soft magnetic materials, Thin films-thickness},
pages = {1539--1542},
file = {ScienceDirect Full Text PDF:E:\Usuarios\Administrator\Zotero\storage\Q42YBTWR\Chechenin et al. - 2005 - Variation of structure and magnetic properties wit.pdf:application/pdf;ScienceDirect Snapshot:E:\Usuarios\Administrator\Zotero\storage\EY24QZM6\S0304885304014830.html:text/html},
}